Centrex® 814
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Centrex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GySXQr_Centrex-814.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Centrex® 814 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in North America. Applications of Centrex® 814 include sporting goods, decorative parts, electrical/electronic applications, household applications and marine applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2100 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 38.6 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3 | 2240 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 75 | J/m | |
| 23°C, 3.18 mm | 270 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C | 8.20 | J | |
| 23°C | 33.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 71.1 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 76.7 | °C | |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 5 |
| RTI Elec (1.50 mm) | 50.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 50.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 238 to 271 | °C | |
| Middle Temperature | 238 to 271 | °C | |
| Front Temperature | 238 to 271 | °C | |
| Nozzle Temperature | 238 to 271 | °C | |
| Processing (Melt) Temp | 238 to 271 | °C | |
| Mold Temperature | 43.3 to 82.2 | °C | |
| Injection Rate | Moderate | ||
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-CO-10GF | Pro Polymers | PP Copolymer | Pro-Comp™ |
| UNITIKA Nylon 66 A125 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Europrene® N 3945 GRN | Versalis S.p.A. | NBR | Europrene® |
| GAPEX® APP30GP08HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| InnoTooling™ IE-9080 | Innovative Polymers, Inc. | TSU | InnoTooling™ |