POTICON BT322

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Otsuka Chemical Co., Ltd.
Trademark:	POTICON
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GyARgS_POTICONBT322.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs.

Advantages

Microscopic reinforcement

Superior friction sliding and wear reduction

Excellent dimensional accuracy and surface smoothness

Highly recyclable

Applications

Automotive Parts (gears, bearings)

LED Reflectors

Watch Parts (gears, ground plane)

Camera (image stabilization parts)

Sliding Parts (gears, wheel bearing)

Camera Module Parts

Motor Parts (cog-wheels, bearings)

BT212N Property: Slide, Low camber

General Information
Features	High Dimensional Stability Low friction coefficient Recyclable materials
Uses	LEDs Gear Application in Automobile Field Camera application Bearing
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.53	g/cm³	ASTM D792
Molding Shrinkage
Flow	1.0	%
Transverse flow	1.3	%
Water Absorption (Equilibrium)	0.070	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	80		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	59.0	MPa	ASTM D638
Tensile Elongation (Break)	2.0	%	ASTM D638
Flexural Modulus	5800	MPa	ASTM D790
Flexural Strength	94.0	MPa	ASTM D790
Coefficient of Friction (vs. Steel - Dynamic)	0.14
Abrasion Loss
-- ¹	14.3	10^-3 mm³/N·km
of counterpart ²	0.00	10^-3 mm³/N·km

Thermal	Nominal Value	Unit	Test Method
Heat Distortion	154	°C	ASTM D648

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	47	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	5.7E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	240 - 270	°C
Mold Temperature	60 - 100	°C
Injection Pressure	50.0 - 100	MPa

Note Message
1 .	Surface pressure: 1MPa
2 .	Slipping velocity: 0.3m/sec

Resin Grade	Manufacturer	Category	Trademark
RTP 203 UV	RTP Company	Nylon 66	RTP
RTP 700 SI 4 Z	RTP Company	HDPE	RTP
Verolloy S1230	PlastxWorld Inc.	PC+ABS	Verolloy
Andur 7003 AP-F	Anderson Development Company	PUR-Ether/TDI	Andur
Sylvin 6930X06 Brown 7454	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin