PPR PA6601
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gy99L8_PPR-PA6601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6/6 33% Glass Fiber Reinforced Heat Stabilized Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 179 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 8970 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 252 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 282 - 304 | °C | |
| Middle Temperature | 277 - 299 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Nozzle Temperature | 266 - 293 | °C | |
| Processing (Melt) Temp | 282 - 299 | °C | |
| Mold Temperature | 38.0 - 93.0 | °C | |
| Injection Pressure | 55.0 - 138 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 41.0 - 103 | MPa | |
| Back Pressure | 0.00 - 1.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: SlowDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR16GY6081 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Europrene Latice® 8487 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Ebalta BLH Epoxy 200 / K 25 | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| POLYFLAM® RIPP 510 D | A. Schulman Europe | PP Copolymer | POLYFLAM® |
| LNP™ LUBRICOMP™ QCP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |