Polifil® PP T-2018 FDA
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gy4DMI_Polifil-PP-T-2018-FDA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® PP T-2018 FDA is a Polypropylene product filled with 20% talc. It is available in North America. Typical application: Food Contact Applications. Primary characteristic: food contact acceptable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.50 mm) | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.0 | % | ASTM D570 |
| Ash Content | 20 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant | 2070 | MPa | |
| Tangent | 2410 | MPa | |
| Flexural Strength (Yield) | 46.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 127 | °C | |
| 1.8 MPa, Unannealed | 65.6 | °C | |
| Continuous Use Temperature 1 | 93.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 104 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Nozzle Temperature | 227 to 232 | °C | |
| Processing (Melt) Temp | 204 to 260 | °C | |
| Mold Temperature | 10.0 to 26.7 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 1040EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| TYNAB® LG30 | Tyne Plastics LLC. | ABS | TYNAB® |
| Vydyne® R525H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Evoprene™ GC 5686 | AlphaGary | SEBS | Evoprene™ GC |
| LEXAN™ 3412HF resin | SABIC Innovative Plastics | PC | LEXAN™ |