TOTAL Polyethylene EVA 1020 VN 3
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gxb9S2_TOTAL-Polyethylene-EVA-1020-VN-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA 1020 VN 3 is made by a high pressure tubular process. Grade for flexible, very transparent films with high strength and very good sealability. Application examples : Thin shrink film for food packaging (coextrusion, lamination...), stretch film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 0.929 | g/cm³ | ISO 1183 |
| -- | 929 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Melt volume-flow rate (190°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 2 |
| Vinyl Acetate Content | 9.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 7.00 | MPa | ISO 527-2 3 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 4 |
| Tensile Elongation at Break | > 50 | % | ISO 527-2 5 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 7.80 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 6.50 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 29.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 380 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 570 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 400 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 79.0 | °C | ISO 306 |
| 50°C/h, B (50N) | 77.0 | °C | ISO 306 6 |
| Melting Temperature (DSC) | |||
| -- | 97.0 | °C | ISO 3146 |
| -- 7 | 98.0 | °C | ISO 11357-3 8 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Elmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 30 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 35 N/mmHaze, ISO 14782, Blown Film, 40 µm: 3.5% |
| Extrusion instructions |
|---|
| Advised Temperature Profile: 150 to 180°CPossible Range of Thicknesses: 20 to 100 µ |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | 10 °C/min |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 402 | RTP Company | PS (GPPS) | RTP |
| Cheng Yu SW10 | Cheng Yu Plastic Company Limited | Acetal (POM) Copolymer | Cheng Yu |
| Ferro PP TPP20AF60GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| ALCOM® PA66 910/1.1 CF15 GF20 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Sylvin 8280-90FU Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |