LNP™ LUBRICOMP™ GL004 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gxa65Q_LNPLUBRICOMPGL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing 20% PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound GL-4040 Product reorder name: GL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Lateral flow : 24 hours | 0.82 | % | ISO 294-4 |
| Traffic : 24 hours | 0.77 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 1860 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 50.3 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2 |
| Fracture | 49.6 | MPa | ASTM D638 |
| Fracture | 47.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.7 | % | ASTM D638 |
| Yield | 4.8 | % | ISO 527-2 |
| Fracture | 5.8 | % | ASTM D638 |
| Fracture | 6.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Stress | 71.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| Dynamic | 0.24 | ASTM D3702 Modified | |
| Static | 0.10 | ASTM D3702 Modified | |
| Wear Factor - Washer | 22.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 3 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.1 | J | ASTM D3763 |
| -- | 5.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 177 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 177 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 162 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 167 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 - 338 | °C | |
| Middle Temperature | 338 - 349 | °C | |
| Front Temperature | 349 - 360 | °C | |
| Processing (Melt) Temp | 360 - 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badaflex® TPE-S 80A 1000 | Bada AG | TPE | Badaflex® |
| Chemlon® 217 GIU | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Estane® 2103-84AEN TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Escorene™ Ultra UL 04028CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| HiFill® PA6/6,6 IM3 BK | Techmer Engineered Solutions | Nylon 66/6 | HiFill® |