Aristech Acrysteel® IMA
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GxMr88_Aristech-Acrysteel-IMA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Acrysteel® IMA is a continuous cast impact acrylic sheet with a matte finish on one side and solvent cementability. The following physical properties were determined using 0.125" (3.17 mm) thickness clear Aristech Acrylics LLC Acrysteel® IMA acrylic sheet. Properties may vary somewhat on other thicknesses and/or colors (translucent or opaque). |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.17 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation, 3.18 mm) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 3.18 mm) | 80 | ASTM D785 | |
| Barcol Hardness (3.18 mm) | 40 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 2510 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.18 mm) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 10 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2620 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (3.18 mm) | 587 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability 2(180°C, 3.18 mm) | No Effect | ASTM D4802 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature (3.18 mm) | 171 to 193 | °C | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 43 | J/m | ASTM D256A |
| Instrumented Dart Impact 3(4.75 mm) | 21.7 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 82.2 | °C | ASTM D648 |
| CLTE - Flow (3.18 mm) | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity 4 | 0.20 | W/m/K | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 5 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 91.0 | % | ASTM D1003 |
| Yellowness Index | ASTM D1925 | ||
| 3.18 mm | 1.8 | YI | |
| 4.75 mm | 2.0 | YI | |
| 5.59 mm | 2.2 | YI |
| Note Message | |
|---|---|
| 1 . | 0.125 in |
| 2 . | 30 min |
| 3 . | FTMS 406-M-1074 |
| 4 . | 0.125 in |
| 5 . | 0.125 in |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V110-60I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TES J-80/10 | Techmer Engineered Solutions | Acetal (POM) Copolymer | TES |
| Arak LLDPE LL0220CA | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Axiall PVC 18780 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Diamond ASA TW18B2 | Network Polymers, Inc. | ASA | Diamond ASA |