Carbo-Rite™ B-263
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Carbo-Rite™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GxErda_Carbo-Rite-B-263.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Carbo-Rite™ B-263 is a carbon black-filled Polypropylene compound with processing aids to improve molding of larger size parts and available in pellet form. Carbo-Rite B-263 solves a wide range of static decay, static shielding and electromagnetic shielding problems. Features: Cost-effective ESD protection, consistent performance, recyclable, durable |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1070 | MPa | ASTM D638 |
| Tensile Strength (Break) | 19.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 1490 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | < 1.0E+6 | ohms·cm | ASTM D257 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | 9.00 | ng/cm² | |
| Anions NO3- | 5.00 | ng/cm² | |
| Anions PO4- | 1.50 | ng/cm² | |
| Anions SO4- | 7.00 | ng/cm² | |
| Outgassing | Internal Method | ||
| MMA | 0.0300 | µg/g | |
| Styrene | < 0.0200 | µg/g | |
| Toluene | < 0.0200 | µg/g | |
| Total Organics | 3.60 | µg/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 AR 5 | RTP Company | PPS | RTP |
| ICORENE® 6446 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| MAJORIS FT200 | AD majoris | PP, Unspecified | MAJORIS |
| Vipel® F774-APT-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| SABIC® PPcompound 15T1020 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |