RAMTOUGH PZ509
| Category: | PC , Polycarbonate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTOUGH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GxCceW_RAMTOUGH-PZ509.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NON TRANSPARENT POLYCARBONATE EASY FLOW FLAME RETARDANT FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.90 | % | ASTM D955 |
| -- | 0.50 - 0.90 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.12 | % | ASTM D570 |
| Saturated, 23°C | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2130 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 120 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2190 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D256 |
| 23°C | 17 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 140 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 130 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+19 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.00 | IEC 60250 | |
| Comparative Tracking Index | 50.0 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Diakon® CMG314N | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Polene EVA MV1030 | TPI Polene Public Company Limited | EVA | Polene EVA |
| Polimid B AV V0M | Poliblend S.p.a. | Nylon 6 | Polimid B |
| KMI KM TEC 132 | KMI Group, Inc. | Acrylic (SMMA) | KMI |
| GELOY™ CR7500 resin | SABIC Innovative Plastics | ASA | GELOY™ |