Borstar® FB1350
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borstar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gx1PwS_Borstar-FB1350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borstar FB1350 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Borstar FB1350 is well suited for mono- and coextrusion of films produced with high neck or low neck extrusion. Borstar FB1350 contains antioxidant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 15 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.60 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD | 500 | MPa | ISO 527-3 |
| TD | 650 | MPa | ISO 527-3 |
| Tensile Strength | ISO 527-3 | ||
| MD | 57.0 | MPa | ISO 527-3 |
| TD | 48.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | 400 | % | ISO 527-3 |
| TD : Fracture | 650 | % | ISO 527-3 |
| Dart Drop Impact | 150 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD | 12.0 | kN/m | ISO 6383-2 |
| TD | 290.0 | kN/m | ISO 6383-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Energy to Resist | 150 | J/cm | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 127 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 5 | ASTM D2457 | |
| Haze | 80 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Die Gap: 1.2 to 1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-89-P808A | Teknor Apex Company | TPE | Telcar® |
| SUMIKASUPER® LCP E6007AS | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Axiall PVC 9113 White 02 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| ICORENE® N6602 | ICO Polymers EMEA, A Division of A. Schulman | ABS | ICORENE® |
| LNP™ THERMOCOMP™ QF0069 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |