LEXAN™ FXD9810 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GwPMYx_LEXAN-FXD9810-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-chlorinated, non-brominated Flame retardant PC-siloxane copolymer blend. Excellent processability, super high flow, good impact, UL rated V-0. Limited translucent colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 30 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 29.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.26 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2150 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Break 3 | 50.0 | MPa | ASTM D638 |
| Break | 49.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.6 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 95 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2100 | MPa | ASTM D790 |
| -- 7 | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 91.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 94.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 49 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 220 | J/m | ASTM D256 |
| 23°C | 690 | J/m | ASTM D256 |
| -30°C 10 | 19 | kJ/m² | ISO 180/1A |
| 23°C 11 | 40 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 63.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 118 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ASTM D1525 12 |
| -- | 137 | °C | ISO 306/B50 |
| -- | 138 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 260 to 282 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ C400TC | Mando Advanced Materials Co., Ltd. | LCP | SEPAZ™ |
| Tarnoform® 500 GF5 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| CONTINUUM™ DGDA-2492N NT | The Dow Chemical Company | HDPE | CONTINUUM™ |
| Karina IVORY PVC COMPOUND 730D35/ 1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRILOY™ D20009 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |