Tarnoform® 200 AST
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnoform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GwLcGr_Tarnoform-200-AST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tarnoform® 200 AST - inherently antistatic injection moulding grade suitable especially for thick-walled applications, where combination of high mechanical and antistatic properties are required. Good antistatic properties are obtained, when moulded parts absorbs enough humidity. Should be used in humid environment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.9 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (2.00 mm) | 2.0 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 12 | % | ISO 527-2/50 |
| Fracture | 25 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2050 | MPa | ISO 178 |
| Flexural Stress 2 | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 120 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 9.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| Melting Temperature | 167 | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | 100 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | mm/min | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | POM-K, M-GNZ, 01-002 | ISO 1874 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 180 - 230 | °C | |
| Mold Temperature | 60.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 200 | °C |
| Extrusion instructions |
|---|
| Slow |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 602 | RTP Company | ABS | RTP |
| PTS PCA-2201NHV | Polymer Technology and Services, LLC | PC+ABS | PTS |
| S&E Wire & Cable GA-1050-OR3-LF | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Baoding 67I95 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| RTP 699 X 143530 | RTP Company | ABS | RTP |