Daplen™ EE158AI
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GwHTZh_Daplen-EE158AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EE158AI is a 13% mineral filled elastomer modified polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Shrinkage 1 | |||
| Anisotropic | 0.090 | % | |
| Isotropic | 0.90 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 h (100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1750 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 170 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 131 | °C | ISO 306/A |
| -- | 55.0 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 to 200 mm/s |
| Note Message | |
|---|---|
| 1 . | radial disk |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® 3K4ELU1 NERO900 | SO.F.TER. SPA | PP Copolymer | Tecnoprene® |
| TEKALOY™ G70NHT | Mando Advanced Materials Co., Ltd. | PC+ABS | TEKALOY™ |
| KRALASTIC® SR | Nippon A&L Inc. | ABS | KRALASTIC® |
| MACOMASS PP MM-PP HI 22 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| Hostacom EKC 330N E1 NAT | LyondellBasell Industries | PP Copolymer | Hostacom |