Promyde® B30 P2 G15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gw1UGr_PromydeB30P2G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde® B30 P2 G15 is a Polyamide 6 injection moulding grade with 15% glass fibre and heat stabilised. CHARACTERISTICS This material is distinguished by high mechanical strength, hardness, rigidity, themostability (melting point 220°C), and resistance to hot lubricants and water. Parts made from Promyde® B30 P2 G15 have particularly high dimensional stability and creep strength. APPLICATIONS High variety of applications field wherever mechanical properties in combinations with thermal resistance is needed. Glass-fiber reinforced grade are suitable for industrial items such as automotive cooling water tanks, lamp socket housings, fans as well as electrical insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.22 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 60.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.60 - 0.90 | -- | % | ISO 294-4 |
| Flow | 0.40 - 0.70 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | 78.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.5 | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 5000 | 2400 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 180 | 90.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 43 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | DIN 53752 | |||
| Flow : 23 to 80°C | 3.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Lateral : 23 to 80°C | 7.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.60 | 6.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.22 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.5 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B12^ NH6 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| StarTUFF TF 75-LR-9 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| VENYL SFRH000R | AD majoris | Nylon 6 | VENYL |
| Nypol® PA A3 T25 FR CNZ0093 NR328 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| AMPLIFY™ GR 209 | The Dow Chemical Company | MAH-g | AMPLIFY™ GR |