Kepital® ET-20A
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KEP Americas |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GviuV9_KepitalET20A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon black filled conductive grade and surface resistivity is less than 10^4 ohm. It has good fuel and chemical resistance and it's suitable for fuel module parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 52.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2450 | MPa | ISO 178 |
| Flexural Stress (23°C) | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarflen® DN-R | Grupa Azoty S.A. | PTFE | Tarflen® |
| UNIPA® Rk | Nytef Plastics, Ltd. | Nylon 66 | UNIPA® |
| Capran Medallion® 1500 film | Honeywell | Nylon 6 | Capran Medallion® |
| HANWHA KL-31 | Hanwha Chemical | PVC, Unspecified | HANWHA |
| Plaslube® ABS 8004 | Techmer Engineered Solutions | ABS | Plaslube® |