POLYFLAM® RPP 2000 E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GunStQ_POLYFLAM-RPP-2000-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame-retardant PP-Compound; halogen free according to DIN VDE 0472 part 815; for extrusion |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 2.00 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 38.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 21 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 109 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 61.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 157 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| Ball Pressure Test (145°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 65.0 | °C | UL 746 |
| 3.00 mm | 65.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 65.0 | °C | UL 746 |
| 3.00 mm | 65.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 65.0 | °C | UL 746 |
| 3.00 mm | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 0.750mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.750 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| 1.50 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 750 | °C | IEC 60695-2-13 |
| 1.50 mm | 750 | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 210 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 MG 20 TFE 10 | RTP Company | PC | RTP |
| VESTAMID® HTplus M3033 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| Viprene™ P55D-22U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| DURACON® M25-45 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Hylon® N2033L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |