Boda BDF201P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GuWIGu_Boda-BDF201P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF201P is a low viscosity curative incorporated fluoroelastomer copolymer. With fast cure speed, this grade is well suited for application where good flowability and excellent mold release property are required. BDF201P can be compounded to meet the major fluoroelastomer specifications. BDF201P can be used for injection molding of O-rings or extrusion of complicated geometries. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 20 | MU | |
| Fluorine Content | 60 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 1.60 | N·m | |
| ML 2(177°C) | 0.200 | N·m | |
| t'90 3(177°C) | 1.7 | min | |
| ts2 4(177°C) | 45.0 | sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 11.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 200 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 16 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACLAR® 11A (3 mil) | Honeywell | PCTFE | ACLAR® |
| Bergamid™ BG6000-8034 RS NC001 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| ASTALOY™ ASA/PET MDA256 | Marplex Australia Pty. Ltd. | ASA+PET | ASTALOY™ |
| Kepital® ES-20 | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Sylvin 8925-80 NATURAL | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |