Ravago Compounds PP-6062

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	Ravago Manufacturing Americas, LLC
Trademark:	Ravago Compounds
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GuPAKg_Ravago-Compounds-PP-6062.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Key Features:

Polypropylene Impact Copolymer

20% Calcium Carbonate filled

General Purpose

Designed for Injection molded applications

Good balance of processability and physical properties

General Information
Filler / Reinforcement	Calcium carbonate filler, 20% filler by weight
Features	Impact copolymer Workability, good Compliance of Food Exposure General
Uses	General
Agency Ratings	FDA 21 CFR 177.1520
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.05	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	20	g/10 min	ASTM D1238
Molding Shrinkage - Flow (23°C)	1.2	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus - Tangent (23°C)	1720	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	110	J/m	ASTM D256

Injection	Nominal Value	Unit
Drying Temperature	71.1 - 93.3	°C
Drying Time	0.0 - 8.0	hr
Rear Temperature	193 - 238	°C
Middle Temperature	193 - 238	°C
Front Temperature	193 - 238	°C
Nozzle Temperature	193 - 238	°C
Mold Temperature	26.7 - 60.0	°C
Back Pressure	0.00 - 0.689	MPa
Screw Speed	50 - 150	rpm

Injection instructions
Hot Runner (if applicable): 420 to 450°F

Resin Grade	Manufacturer	Category	Trademark
MARPOL® Homo 20.NA	Marco Polo International, Inc.	PP Homopolymer	MARPOL® Homo
XYLEX™ X8303CL resin	SABIC Innovative Plastics Europe	PC+Polyester	XYLEX™
Derakane® 470-36-S	Ashland Performance Materials	Vinyl Ester	Derakane®
LG PVC LS100E	LG Chem Ltd.	PVC Homopolymer	LG PVC
Versaflex™ CL2000X	PolyOne Corporation	TPE	Versaflex™