POLYFLAM® RPP 374 ND CS1 5V
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GtdDcV_POLYFLAM-RPP-374-ND-CS1-5V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% talc filled flame-retardant PP-Homopolymer; without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.8 | kJ/m² | ISO 179/1eA |
| 23°C | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 12 | kJ/m² | ISO 179/1eU |
| 23°C | 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 118 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 92.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 105 | °C | UL 746 |
| 1.80 mm | 105 | °C | UL 746 |
| 3.00 mm | 105 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 105 | °C | UL 746 |
| 1.80 mm | 105 | °C | UL 746 |
| 3.00 mm | 105 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 105 | °C | UL 746 |
| 1.80 mm | 105 | °C | UL 746 |
| 3.00 mm | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 1.80 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | UL 746 | |
| 1.80 mm | PLC 3 | UL 746 | |
| 3.00 mm | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 1.80, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 5VA | UL 94, IEC 60695-11-10, -20 | |
| 1.80 mm | 5VA | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 1.80 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 750 | °C | IEC 60695-2-13 |
| 1.80 mm | 750 | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4799 X 121826 C | RTP Company | Polyester Alloy | RTP |
| Alpha PVC GW 2462-H VW1 NAT LCF | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| GAPEX® RPP20EC12BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Geon™ Vinyl Flexible R158AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina BLACK PVC COMPOUND 851-48/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |