| Hifax CA244 high melt flow, 850 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, processability and dynamic impact characteristics. It was designed primarily for use in painted automotive exterior trim applications where material flow is an important consideration. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 14 | % | ISO 527-2 |
| Flexural Modulus | 850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 3.9 | kJ/m² | |
| 23°C | 33 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 47.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 8.0E-5 | cm/cm/°C | ASTM E228, ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 9812A-03 | Colorite Polymers | PVC, Flexible | Unichem |
| ADEKA ED-509S | Adeka Corporation | Epoxy | ADEKA |
| Dryflex® 660900S | ELASTO | SEBS | Dryflex® |
| FUDOWPREMIX® FP100F typeA | Fudow Co., Ltd. | Polyester, TS | FUDOWPREMIX® |
| TAFMER™ DF840 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |