CONATHANE® EN-1554
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Cytec Industries Inc. |
| Trademark: | CONATHANE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GtWsxb_CONATHANE-EN-1554.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONATHANE EN-1554 is a polyether based polyurethane resin system primarily intended for use as a molding, encapsulating and potting compound for harness breakouts, watertight electrical connectors, cables, cable end seals, printed circuitry and other electrical components. The system also has utility in the casting or molding of mechanical parts and as a lining material for pumps, chutes and conveyors, where outstanding abrasion resistance is a necessity. CONATHANE EN-1554 may be cured at room or elevated temperatures. CONATHANE EN-1554, when fully cured, is a tough, cold-flow resistant elastomer that has good resistance to oils, gasoline, JP-4 fuel, water, and seawater and also provides outstanding protection against corrosion or contamination. The system is funginert when tested in accordance with MIL-E-5262C and MIL-STD-810B. Three primers have been developed for use in bonding EN-1554 to metals, neoprene, and polyvinyl chloride during the curing process. CONAP® AD-1146 is recommended for metals, CONAP® PR-1167 for neoprene, and CONAP® AD-1161 for polyvinyl chloride. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.09 | g/cm³ | |
| -- 2 | 0.998 to 1.20 | g/cm³ | |
| Water Absorption - 24 hour immersion in D.I. water @ 200°F | 0.33 | % | |
| Shrinkage - Volume | 4.5 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Fungal Resistance | Non-nutrient | ||
| Isocyanate Content 3 | 4.9 to 5.3 | % | |
| Non-Volatile Content - Mixed System | 100 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 to 90 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 300% Secant | 7.58 | MPa | Internal Method |
| Tensile Strength | 31.0 | MPa | |
| Tensile Elongation (Break) | 550 | % |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 61.3 | kN/m | |
| Compression Set (70°C, 22 hr) | 50 | % |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength (70°C, 336 hr, in Water) | -11 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- 5 | 2.5E+10 | ohms | |
| -- 6 | 2.5E+12 | ohms | |
| Volume Resistivity | |||
| 25°C | 5.1E+12 | ohms·cm | |
| 121°C | 6.3E+10 | ohms·cm | |
| Dielectric Strength | |||
| 1.27 mm | 24 | kV/mm | |
| 3.18 mm | 12 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 6.63 | ||
| 25°C, 1 MHz | 5.23 | ||
| Arc Resistance | 120 | sec | |
| Insulation Resistance (25°C) | 5.8E+11 | ohms |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 33 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Thermoset Mix Viscosity | |||
| 25°C 7 | 15000 | cP | |
| 25°C 8 | 20000 | cP |
| Note Message | |
|---|---|
| 1 . | Mix |
| 2 . | Hardener |
| 3 . | Resin |
| 4 . | Die C |
| 5 . | 250°F |
| 6 . | 77°F |
| 7 . | Hardener |
| 8 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DIC.PPS FZ-820 | DIC Corporation | PPS | DIC.PPS |
| KumhoSunny ABS 770SRS | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| LNP™ THERMOCOMP™ WF008 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| Pinnacle PP 1120 Z | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |
| Tribocomp® PA66 LGF30 PTFE18 N6 | Solvay Specialty Polymers | Nylon 66 | Tribocomp® |