Lupoy® GP5106F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GtFgBg_Lupoy-GP5106F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Flame Retardance Application IT/OA(Housing) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1240 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (260°C/5.0 kg) | 26.2 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.11 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 4000 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 3.20 mm 5 | 65.7 | MPa | ASTM D638 |
| Break | 77.0 | MPa | ISO 527-2 6 |
| Tensile Elongation | |||
| Break, 3.20 mm 7 | 7.0 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2 8 |
| Flexural Modulus 9(3.20 mm) | 3920 | MPa | ASTM D790 |
| Flexural Strength 10(3.20 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 11 | ||
| -30°C | 4.90 | kJ/m² | |
| 23°C | 6.80 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 12 | ||
| -30°C | 29.5 | kJ/m² | |
| 23°C | 35.4 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa | 125 | °C | ISO 75-2 13 |
| 1.8 MPa, Unannealed, 6.40 mm | 113 | °C | ASTM D648 |
| 1.8 MPa | 109 | °C | ISO 75-2 14 |
| Glass Transition Temperature 15 | 140 | °C | ISO 11357-2 16 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 117 | °C | ISO 306 17 |
| CLTE | ISO 11359-2 18 | ||
| Flow | 4.5E-5 | cm/cm/°C | |
| Transverse | 7.8E-5 | cm/cm/°C | |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 19 |
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 20 |
| Electric strength | 29 | kV/mm | IEC 60243-1 21 |
| Relative Permittivity (1 MHz) | 3.10 | IEC 60250 22 | |
| Dissipation Factor (1 MHz) | 0.010 | IEC 60250 23 | |
| Comparative tracking index | 200 | IEC 60112 24 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.70 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Burning Behav. at thickness h (1.70 mm, UL) | V-0 | ISO 1210 25 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 235 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.0196 to 0.0588 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 5.0 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 5.0 mm/min |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 1.3 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | 10 °C/min |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 24 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 25 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PP GFPP40-3 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| TEKANATE™ G7013 | Mando Advanced Materials Co., Ltd. | PC | TEKANATE™ |
| Cevian®-V 510, 510SF | Daicel Polymer Ltd. | ABS | Cevian®-V |
| Sylvin 6248-80 Yellow 4177 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CYCOLOY™ CX2142ME resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |