LONGLITE® PBT 7020-104X
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GsNW6F_LONGLITE-PBT-7020-104X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/ASA 7020-104X is a 20% glass fiber reinforced black color injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 to 1.3 | % | |
| Flow | 0.10 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 20 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C) | 220 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 2830 | Huntsman Corporation | PAO | REXtac® APAO |
| TECHNOGRAN® IONOMERE NAT CLEAR | Eurocompound Polymers | Ionomer | TECHNOGRAN® |
| Clariant Nylon 6/6 PA-113CF30 TF15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Chemraz 644 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Hylex® P1017FR | Entec Polymers | PC | Hylex® |