A high melt index vinyl acetate polyethylene Applications:
Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 50.9 | MPa | |
| 1% Secant, TD | 55.3 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 21.6 | MPa | |
| TD : Break | 15.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 530 | % | |
| TD : Break | 810 | % | |
| Dart Drop Impact | 94 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 240 | g | |
| TD | 330 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 53.9 | °C | ASTM D1525 |
| Peak Melting Temperature | 83.9 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 89 | ASTM D2457 | |
| Haze | 0.90 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon F2538H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| Ultraform® N 2640 E2 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Yuyao PP TL603 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Lusin® Alro OL 153 S | Chem-Trend L.P. | Silicone | Lusin® |
| Moplen HP400H | LyondellBasell Industries | PP Homopolymer | Moplen |