Durethan® T 7141 00000
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GsCckv_Durethan-T-7141-00000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.70 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 280°C, 2.00 mm 1 | 0.70 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | % | |
| Flow : 280°C, 2.00 mm 3 | 0.20 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 11000 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 175 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PET+PBT, GHMR, 07-120, (GF+MD) 40 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B120 |
| Melting Temperature 8 | 260 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 5.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 750 | °C | |
| 1.50 mm | 750 | °C | |
| 3.00 mm | 750 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | |
| 1.50 mm | 775 | °C | |
| 3.00 mm | 775 | °C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 100 to 130 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® S4730 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TECASINT™ 2021 | Ensinger Inc. | PI, TP | TECASINT™ |
| ASTALAC™ ASA 202 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| LNP™ VERTON™ UV00ASU compound | SABIC Innovative Plastics | PPA | LNP™ VERTON™ |
| POLYFLAM® RIPP 4000 OSD K3014 | A. Schulman Europe | PP Copolymer | POLYFLAM® |