LNP™ COLORCOMP™ C1200HFC compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Grx7RF_LNPCOLORCOMPC1200HFCcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* C1200HFC is a compound based on PC+ABS. Added features of this grade include: Excellent Flow, Impact, High Heat Resistance, Low Temperature Ductility. For use in automotive, appliance and electrical components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 24.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2280 | MPa | ASTM D638 |
| -- | 2370 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.2 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 5.0 | % | ASTM D638 |
| Yield | 4.8 | % | ISO 527-2/50 |
| Fracture 4 | 150 | % | ASTM D638 |
| Fracture | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 5 | 2340 | MPa | ASTM D790 |
| -- | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 86.0 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 480 | J/m | ASTM D256 |
| 23°C | 590 | J/m | ASTM D256 |
| -30°C 7 | 34 | kJ/m² | ISO 180/1A |
| 23°C 8 | 49 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 54.2 | J | ASTM D3763 |
| 23°C, Total Energy | 54.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 129 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 113 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 110 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (-40 to 40°C) | 7.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.2 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4mm, Cut |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 103HSL BKB080 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| AKROMID® B3 GF 15 1 L natural (4690) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| APEX® 3601-90 | Teknor Apex Company | PVC, Flexible | APEX® |
| Kemcor LDX 438 | Qenos Pty Ltd | LLDPE | Kemcor |
| Hostalen PP H2150 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |