Kingfa PA66-ROW
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GrWNW1_Kingfa-PA66-ROW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PA66-ROW is a polyamide 66 (nylon 66) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PA66-ROW are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 1.1 | % | ASTM D955 |
| Transverse flow : 23°C | 1.4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.8 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 3200 | MPa | ASTM D790 |
| Flexural Strength 4 | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 72 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 240 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 95.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 235 - 245 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Processing (Melt) Temp | 245 - 265 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Processing Temperature Limit: 270°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex EPM P | Ravago Group | EPM | Ravaflex |
| Xuchuan XCW-8225H-12 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ELASTOSIL® AUX PRIMER G 3241 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| EPLAMID 66 GFS 50 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Kazan LDPE 15313-003 OKP 22 1111 2003 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |