DuraGrip® DGR 6165TR
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Advanced Polymer Alloys |
| Trademark: | DuraGrip® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gqy0IA_DuraGrip-DGR-6165TR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DuraGrip® DGR6165TR is a translucent thermoplastic elastomer (TPE) formulated for excellent elastic properties and enhanced adhesion to engineered thermoplastics using insert molding, co-injection molding and co-extrusion processes. DGR6165TR bonds tenaciously to polycarbonate, polycarbonate alloys, ABS, ASA, acrylics, and cellulosic materials. It will also bond to various nylons and PET. DGR6165TR is hygroscopic and drying is recommended at 150F for 3 to 4 hours to ensure optimum aesthetics, properties and adhesion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D471, ISO 2781 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 11 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 65 | ASTM D2240, ISO 48 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 3.97 | MPa | |
| Flow : 100% Strain | 3.43 | MPa | |
| Across Flow : 300% Strain | 9.23 | MPa | |
| Flow : 300% Strain | 7.73 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 25.9 | MPa | |
| Flow : Break | 18.1 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 810 | % | |
| Flow : Break | 580 | % | |
| Tear Strength 1 | ASTM D624 | ||
| Across Flow | 59.5 | kN/m | |
| Flow | 52.2 | kN/m |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (190°C, 294 sec^-1) | 427 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech P706 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Ultramid® B3M6 BK60564 | BASF Corporation | Nylon 6 | Ultramid® |
| Geon™ HTX M6215 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| POLYfill PPH T4060 | Polykemi AB | PP Homopolymer | POLYfill |
| LNP™ STAT-KON™ EE004 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |