Sarlink® TPE TPE EE-2265B-01 BLACK
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gqry59_Sarlink-TPE-TPE-EE-2265B-01-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE TPE EE-2265B-01 BLACK is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 69 | ASTM D2240 | |
| Shaw A, 15 seconds | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 37.9 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain | 1.86 | MPa | ASTM D412 |
| Flow : 100% strain | 2.62 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture | 8.41 | MPa | ASTM D412 |
| Flow : Fracture | 5.93 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture | 810 | % | ASTM D412 |
| Flow : Fracture | 660 | % | ASTM D412 |
| Tear Strength | 30.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 20 | % | ASTM D395 |
| 70°C, 22 hr | 37 | % | ASTM D395 |
| 125°C, 70 hr | 73 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | -7.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (100°C, 168 hr) | -0.20 | % | ASTM D573 |
| Change in Durometer Hardness in Air (Shore A) | 1.0 | ASTM D573 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.03 mm) | 51 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Change in Tear Strength in Air(100oC,168hr)+ 2% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS VL-2 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| TECAMID™ 66 | Ensinger Inc. | Nylon 66 | TECAMID™ |
| Colorite CS Series CS7559LS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Hypro® PP-RP 35/1.5C | Entec Polymers | PP Random Copolymer | Hypro® |
| LubriOne™ NI-20GF/15T FR | PolyOne Corporation | Nylon 610 | LubriOne™ |