LNP™ THERMOCOMP™ QF006 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gq8X15_LNP-THERMOCOMP-QF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound QF-1006 Product reorder name: QF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.98 to 0.99 | % | ISO 294-4 |
| Flow : 24 hr | 0.17 to 0.18 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.33 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8410 | MPa | ASTM D638 |
| -- | 8800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 150 | MPa | ASTM D638 |
| Break | 153 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.6 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7860 | MPa | ASTM D790 |
| -- | 7800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 251 | MPa | ASTM D790 |
| -- | 219 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 9.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 72 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.93 | J | ASTM D3763 |
| -- | 2.72 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 221 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 207 | °C | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME B V2Y 15 SL5 | RIALTI Srl | PP, Unspecified | RIALFLAME |
| Syncure™ System S110FV-UV | PolyOne Corporation | XLPE | Syncure™ |
| Ultra Purge PET-E | Moulds Plus International USA, Inc. | Proprietary | Ultra Purge |
| ESTADIENE 1016 T V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Formolon® AW04 | Formosa Plastics Corporation, U.S.A. | PVC, Rigid | Formolon® |