FLEXAREN® 18000
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Innospec Leuna GmbH |
| Trademark: | FLEXAREN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GptDR3_FLEXAREN-18000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FLEXAREN® 18000 - high quality ethylene vinyl acetate copolymer with 18% content of vinyl acetate. Manufactured by high pressure tubular process FLEXAREN® 18000 is more elastic than LDPE and compatible with a wide range of polymers. It can be processed with the same equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 0.939 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 89 | ||
| Shore D | 36 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1BA | ||
| Break | 26.0 | MPa | |
| 50% Strain | 4.50 | MPa | |
| Tensile Strain (Break) | > 750 | % | ISO 527-2/1BA |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 37.0 | MPa | |
| TD : 50 µm | 27.0 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 66.0 | °C | ISO 306/A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 100 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 60002 | Teknor Apex Company | PVC, Flexible | APEX® |
| DINAPLEN® PPH1S07 G40 HUV-1013 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| EPLAMID 66 GFS 50 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| LEXAN™ SLD3000 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Petrothene® NA420234 | LyondellBasell Industries | LDPE+EVA | Petrothene® |