KEPAMID 2320CF is a carbon fiber 20%-reinforced conductive PA66 grade.

It has good mechanical properties, heat resistance, wear resistance, and electrical properties.

It is suitable for automotive, electrical & electronics, and industrial parts requiring high stiffness, heat resistance, and conductivity.

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 20% filler by weight
Features	Rigidity, high Good electrical performance Good wear resistance Heat resistance, high
Uses	Electrical/Electronic Applications Industrial components Application in Automobile Field
RoHS Compliance	RoHS compliance
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.22	g/cm³	ISO 1183

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	120		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	245	MPa	ISO 527-2
Tensile Strain (Break)	2.0	%	ISO 527-2
Flexural Modulus	14300	MPa	ISO 178
Flexural Stress	340	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	9.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	250	°C	ISO 75-2/B
Melting Temperature ¹	260	°C	ISO 11357-3

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+3	ohms·cm	IEC 60093
Relative Permittivity (1 MHz)	3.60		IEC 60250

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.8 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature
--	90	°C
Dry Air Dryer	80	°C
Drying Time
--	6.0 - 8.0	hr
Dry Air Dryer	4.0 - 6.0	hr
Suggested Max Moisture	0.050	%
Hopper Temperature	60 - 80	°C
Rear Temperature	280	°C
Middle Temperature	285	°C
Front Temperature	285	°C
Nozzle Temperature	290	°C
Mold Temperature	70 - 90	°C
Back Pressure	0.490 - 0.981	MPa
Screw Speed	80 - 120	rpm

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Teldene® H03ML	National Petrochemical Industries Company (NATPET)	PP Homopolymer	Teldene®
Staramide PX06093	Eurostar Engineering Plastics	Nylon 6	Staramide
Vi-Chem PVC VDM87-30E	Vi-Chem Corporation	PVC, Unspecified	Vi-Chem PVC
Braskem PE GM 7746 C	Braskem	HDPE	Braskem PE
Exelene® HDPE 8000	Montachem International, Inc.	HDPE	Exelene® HDPE