Wellamid® GF14-60 XE-NBK1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GpgZiu_Wellamid-GF14-60-XE-NBK1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® GF14-60 XE-NBK1 is a Polyamide 6 (Nylon 6) material filled with 14% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Typical application of Wellamid® GF14-60 XE-NBK1: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.80 to 1.2 | % | |
| Flow : 23°C | 0.50 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551000-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Vi-Chem PVC V147-70 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Latamid 66 H2 G/25-V0KB1 | LATI S.p.A. | Nylon 66 | Latamid |
| ESTOPLAST XU 6430IY01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| Sylvin 7833-75 Red 6260 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |