Westlake LDPE EF706AA
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gpftsp_WestlakeLDPEEF706AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF706AA is a LDPE resin suggested for blown or cast film applications where stiffness and machinability are important. Application/Uses
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 165 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 24.1 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 19.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 600 | % | ASTM D882 |
| Dart Drop Impact (51 µm, Blown Film) | 170 | g | ASTM D1709 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 2.0 mils; blow up ratio 2.5:1, die gap 35 mils. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 210 | °C |
| Extrusion instructions |
|---|
| Cast Film Melt Temperature: 520 to 550°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPTFFR-2 | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP PP |
| Gallonprene® GP520-6516 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GAPEX® APP30GP04BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| EPLAMID 66 GFS 50 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Lasulf LASULF G/20 | LATI S.p.A. | PSU | Lasulf |