LUVOCOM® 1105-8716/L Datasheet,PEEK,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1105-8716/L is a polyetheretherketone (PEEK) material, which contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1105-8716/L are: Flame Retardant Good stiffness chemical resistance Heat resistance Hydrolytic stability Typical application areas include: textile/fiber engineering/industrial accessories Aerospace Automotive Industry medical/health care

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Rigid, good Good liquidity Good strength Good chemical resistance Heat resistance, high Hydrolysis stability Flame retardancy
Uses	Textile applications Engineering accessories Aerospace applications Application in Automobile Field Medical/nursing supplies
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.38	g/cm³	ISO 1183
Molding Shrinkage	0.40 - 0.90	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	7000	MPa	ISO 527-2
Tensile Stress (Break)	138	MPa	ISO 527-2
Tensile Strain (Yield)	2.6	%	ISO 527-2
Flexural Modulus	6500	MPa	ISO 178
Flexural Stress	225	MPa	ISO 178
Flexural Strain at Flexural Strength	3.6	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	260	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+14	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	45	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	275	°C	ISO 75-2/A
Continuous Use Temperature	250	°C	UL 746B
Vicat Softening Temperature	320	°C	ISO 306/A
CLTE - Flow	3.0E-5	cm/cm/°C	DIN 53752

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+13	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	150	°C
Hot air dryer, B	120	°C
Drying Time
Hot air dryer, A	3.0 - 6.0	hr
Hot air dryer, B	6.0 - 8.0	hr
Rear Temperature	360 - 370	°C
Middle Temperature	380 - 390	°C
Front Temperature	390 - 400	°C
Nozzle Temperature	360 - 380	°C
Processing (Melt) Temp	390	°C
Mold Temperature	170 - 200	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PEEK , Polyetheretherketone
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GpV5ok_LUVOCOM11058716L.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Rilsan® BMN P20 D	Arkema	Nylon 11	Rilsan®
Quadrant EPP TIVAR® 1000 Black Virgin	Quadrant Engineering Plastic Products	UHMWPE	Quadrant EPP
Lupoy® 1301-22	LG Chem Ltd.	PC	Lupoy®
MARPOL® HDB 505	Marco Polo International, Inc.	HDPE, HMW	MARPOL®
Alpha PVC 3006-95	Mexichem Specialty Compounds Inc.	PVC, Unspecified	Alpha PVC