PALMID® R 6 E
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | pal plast GmbH |
| Trademark: | PALMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GpBFmk_PALMID-R-6-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PALMID®R 6 E is a polyamide 6 (nylon 6) product,. It can be processed by extrusion and is available in Europe. Typical application areas are: hoses. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 8.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.9 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield, 23°C) | 87.5 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break (23°C) | 50 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 202 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2800 to 3000 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 85 to 90 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 5 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 6 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 200 to 204 °CDensity, ISO 1183: 1.12 to 1.14 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 8 to 9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 2.8 to 3 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 509 | Marco Polo International, Inc. | HDPE | MARPOL® |
| AKROMID® A3 GF 20 1 black (2307) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ALCUDIA® LDPE CA-2130A | REPSOL | LDPE | ALCUDIA® LDPE |
| MACOMASS PP MM-PP HI 21 (20% Talc) | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| LEXAN™ 203R resin | SABIC Innovative Plastics | PC | LEXAN™ |