Syncure™ System S100NA
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GoycW8_Syncure-System-S100NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Syncure™ systems are two part moisture crosslinkable compounds, UL bulletinized, RoHS compliant, easy processing, high strength, colorable cable insulation compound suitable for service entrance cables. Graft resin component of this system has approximate shelf life of 6 months from the date of production. Please consult PolyOne for its use past 6 months. |
| General Information | |
|---|---|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Gel Content 1 | 72 | % | ASTM D2765 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention rate | |||
| 121°C, 1.91 mm 2 | 95 | % | |
| 158°C, 1.91 mm 3 | 90 | % | |
| Elongation retention rate | |||
| 121°C, 1.91 mm 4 | 90 | % | |
| 158°C, 1.91 mm 5 | 85 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation (131°C) 6 | 10 | % | UL 1581 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Catalyst parent mixture- S-1010B 7 | 5.0 | % | |
| Transplant-based resin- S-1054A 8 | 95 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 52 | ASTM D2240 | |
| Shaw D, 10 seconds | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 9(Yield) | 19.3 | MPa | ASTM D638 |
| Tensile Elongation 10(Break) | 400 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UL Temperature Rating | 90 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 39 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.14 | ASTM D150 | |
| Dissipation Factor | 2.0E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| 注释：以上情况代表了在30密耳壁的14 AWG上测量得出的典型属性。存放和搬运：包装打开之后应在48小时之内使用，避免自硬化和报废。 |
| Note Message | |
|---|---|
| 1 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 2 . | 336 hours, UL standard |
| 3 . | 168 hours, UL standard |
| 4 . | 336 hours, UL standard |
| 5 . | 168 hours, UL standard |
| 6 . | 500g,1 hour |
| 7 . | S-1010B |
| 8 . | S-1025A or S-1054A |
| 9 . | Type 4, 510mm/min |
| 10 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R84/21 | Spartech Plastics | PMMA+PVC | Royalite |
| Andur 9002 APTF/Curene® 107 | Anderson Development Company | PUR-TDI | Andur |
| Devcon Plastic Welder™ | Devcon | Epoxy | Devcon |
| Kelon® A H CEG/40 | LATI S.p.A. | Nylon 66 | Kelon® A |
| Sylvin 916VO-95 Grey 9393 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |