VECTRA® E115i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GokaNt_VECTRA-E115i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
15% glass reinforced Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant. FDA compliant UL-Listing V-0 black at 0.75mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | -0.20 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 43 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 175 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 298 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 252 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 202 | °C | ISO 306/B50 |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 33 | kV/mm | IEC 60243-1 |
| Relative Permittivity (2.05 GHz) | 3.94 | Internal method | |
| Dissipation Factor (2.05 GHz) | 5.0E-3 | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 335 | °C | |
| Middle Temperature | 320 - 340 | °C | |
| Front Temperature | 325 - 355 | °C | |
| Nozzle Temperature | 335 - 350 | °C | |
| Processing (Melt) Temp | 335 - 355 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 335 to 345°CZone 4 Temperature: 330 to 360°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene Lumicene® MR 30MC2 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Braskem PP PH 0952 | Braskem | PP Homopolymer | Braskem PP |
| LNP™ THERMOCOMP™ FX93387L compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ THERMOCOMP™ |
| Pearlthane® CLEAR 15N80 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |
| Hostacom M2 T02 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |