Category: | PP Homopolymer , Polypropylene Homopolymer |
Manufacturer: | Polykemi AB |
Trademark: | POLYfill |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | GoQ3wp_POLYfill-PPH-B8065.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Mineral reinforced |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.86 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.1 to 1.4 | % | |
Flow | 1.1 to 1.4 | % |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress | 18.0 | MPa | ISO 527-2 |
Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 3200 | MPa | ISO 178 |
Flexural Stress | 35.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature 1 | |||
0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
Vicat Softening Temperature | |||
-- | 150 | °C | ISO 306/A50 |
-- | 100 | °C | ISO 306/B50 |
Note Message | |
---|---|
1 . | 120°C/hr |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Quantum Composites QC-7753 | Quantum Composites Inc. | Polyester, TS | Quantum Composites |
Delta LDPE 20018 | Delta Polymers | LDPE | Delta |
DINALON® A3S25 | Grupo Repol | Nylon 66 | DINALON® |
ELASTOSIL® R plus 533/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
Sylvin 2991-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |