SCHULAMID® 66 GB 30 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GoP80Q_SCHULAMID-66-GB-30-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass bead reinforced, heat stabilized Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 185 | 125 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4500 | 2500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 95.0 | 65.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 7.5 | 11 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 235 | -- | °C | ISO 306/A50 |
| -- | 230 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | |
| 3.00 mm | -- | 650 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo PP FY3011E | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| Hyundai EP PA6 LS240 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Karina GRAY PVC COMPOUND 700-DA-18/291-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TechnoMid PA6 S GF 15 | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| POCAN® T 7323 POS151 000000 | LANXESS GmbH | PBT+PET | POCAN® |