DENKA Transparent Polymer TH-11
| Category: | MMBS , Methyl Methacrylate Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Transparent Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Go3NiY_DENKA-Transparent-Polymer-TH-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA Transparent Polymer TH-11 is a Methyl Methacrylate Butadiene Styrene (MMBS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200°C/5.0 kg | 5.2 | g/10 min | |
| 220°C/10.0 kg | 76 | g/10 min | |
| Molding Shrinkage (2.00 mm) | 0.40 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 34 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2/5 |
| Nominal Tensile Strain at Break | 36 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2250 | MPa | ISO 178 |
| Flexural Stress 2 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 64.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 84.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 91.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 2.6 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 180 to 220 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3875H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Unichem 7512G-05 | Colorite Polymers | PVC, Unspecified | Unichem |
| AKROMID® A3 GF 50 natural (2423) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| EL-Lene™ H6670B | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Petrotene® PP A3 G40 NTLA010 PH306 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |