Desmopan® 453 DPS 041
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GnxNRT_Desmopan-453-DPS-041.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding grade; grease and oil-resistant; hydrolysis-stabilised; low compression set; good wear resistance; Application; Injection molded engineering parts; Automotive engineering; Coupling elements |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1230 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 97 | ||
| Shore D, 15 sec | 51 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 37.9 | MPa | |
| 10% Strain, 23°C | 8.20 | MPa | |
| 50% Strain, 23°C | 15.1 | MPa | |
| 100% Strain, 23°C | 18.3 | MPa | |
| 300% Strain, 23°C | 30.6 | MPa | |
| Tensile Strain 4(Break, 23°C) | 470 | % | DIN 53504 |
| Abrasion Resistance | 32.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 1.78 | GPa | |
| 20°C | 0.240 | GPa | |
| 60°C | 0.110 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience | 30 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5 | 180 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 15 | % | |
| 70°C, 24 hr | 27 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2010 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| SCANAMID 6 B12^ QF2515 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| ADFIL 230 | Pooya Polymer Tehran | Polyolefin, Unspecified | ADFIL |
| ASTALOY™ PC/PET C70L9 | Marplex Australia Pty. Ltd. | PC+PET | ASTALOY™ |
| Karina IVORY PVC COMPOUND -E 105803-35/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |