FARALLOY® ABS-105
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | O'Neil Color and Compounding |
| Trademark: | FARALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gnknrc_FARALLOY-ABS-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FARALLOY ABS-105 is a flame retardant sheet extrusion grade ABS formulated to resist ignition as defined by Underwriters' Laboratories 94V test protocol. This product is non-blooming and has enhanced resistance to discoloration caused by interior lighting. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 35.9 | MPa | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | ||
| 2.21 mm | 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 810CI | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| THERMOLAST® K TC4MSZ (Series: AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Nanjing Hongrui PA6 B860 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| ECP 21150 | TBA Electro Conductive Products Ltd. | TPU-Polyether | ECP |
| HAIPLEN H10 T4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |