Starflam M10009AP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gnbmn6_Starflam-M10009AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam M10009AP is an Unfilled Flame Retardant high fluidity Polypropylene (Homo) Injection Molding Resin |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (4.00 mm) | 1.6 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 36.0 | MPa | |
| Break | 23.0 | MPa | |
| Tensile Strain (Yield) | 7.2 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1900 | MPa | ISO 178 |
| Flexural Stress | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 44 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 57.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Processing (Melt) Temp | 190 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP H7526 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Spartech Polycom SC1-4099 | Spartech Polycom | ABS | Spartech |
| VALOX™ 315 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| HiFill® ABS GF10 LE | Techmer Engineered Solutions | ABS | HiFill® |
| Pearlthane® ECO D12T55D | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® ECO |