Sindustris PBT SV1081
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GnTD8i_Sindustris-PBT-SV1081.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT SV1081 is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris PBT SV1081: High Viscosity. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 2.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 57.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 154 | °C | |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 235 to 245 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 225 to 245 | °C | |
| Cylinder Zone 2 Temp. | 230 to 250 | °C | |
| Cylinder Zone 3 Temp. | 240 to 260 | °C | |
| Cylinder Zone 4 Temp. | 240 to 260 | °C | |
| Adapter Temperature | 240 to 260 | °C | |
| Melt Temperature | 225 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B15 P | NUREL, S.A. | Nylon 6 | Promyde® |
| Resinoid 1365 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| NuSil CV1-2960 | NuSil Technology | Silicone | NuSil |
| Formolon® 40 | Formosa Plastics Corporation, U.S.A. | PVC Alloy | Formolon® |
| 3M™ Dyneon™ Fluoroelastomer FPO 3630 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |