LG ABS MA210
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gn90On_LG-ABS-MA210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Low Gloss Application Automotive Sheet, Semi-Conductor Tray |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 60 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 70.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 69 | J/m | ASTM D256 |
| -20°C, 6.40 mm | 59 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 6.40 mm) | 91.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 2.50 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 200 - 230 | °C | |
| Cylinder Zone 4 Temp. | 200 - 230 | °C | |
| Adapter Temperature | 200 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| Top RollStack Temperature: 70 to 100°CMiddle RollStack Temperature: 70 to 90°CBottom RollStack Temperature: 60 to90°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 18.6kg |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-IM-G30 | Polymer Resources Ltd. | PBT | PRL |
| Sylvin 7840-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nipol® NBR N21 | Zeon Corporation | NBR | Nipol® NBR |
| WELLAMID Nylon 6600/42 GS 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Sylvin 6229-70LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |