Riblene® FH 39 D
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GmypRq_Riblene-FH-39-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FH 39 D is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FH 39 F is characterised by a good balance between processability and mechanical properties. Main Application Riblene FH 39 D is recommended for general packaging film and for diapers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 30 to 100 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 40 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 40 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 24.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 23.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 400 | % | |
| TD : Break, 40 µm, Blown Film | 600 | % | |
| Dart Drop Impact 1(40 µm, Blown Film) | 140 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 60.0 | kN/m | |
| TD : 40.0 µm | 55.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 114 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 71 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 62 N TS | Plastcom | PP, Unspecified | SLOVALEN® |
| Moplen RP348S | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Tarnamid® T- 29 MCS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| NOVAPOL® HB-L354-A | NOVA Chemicals | HDPE | NOVAPOL® |
| Sylvin 8382-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |