EPO-TEK® B9101-2 Unfilled
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GmquCM_EPO-TEK-B9101-2-Unfilled.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A single component, electrically and thermally insulating epoxy designed for adhesive, sealing and potting of micro-electronics and semiconductor devices. It can be used in many industries such as military, automotive, optical or medical electronics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 80.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.6E-5 | cm/cm/°C | |
| -- 3 | 1.9E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.542 | ||
| Transmittance | |||
| 340 nm | 73.0 | % | |
| 420 to 1600 nm | > 87.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 5 | 52 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 340 | °C | |
| Die Shear Strength - >20 kg (23°C) | 46.9 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 150 | °C | |
| Intermittent | -55 to 250 | °C | |
| Storage Modulus (23°C) | 1.99 | GPa | |
| Weight Loss on Heating | |||
| 250°C | 1.6 | % | |
| 300°C | 2.5 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | White | ||
| Density | 1.19 | g/cm³ | |
| Viscosity 6(23°C) | 1.0 to 1.3 | Pa·s | |
| Curing Time (180°C) | 1.0 | hr | |
| Pot Life | 40000 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 88 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Refrigerated |
| 6 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nordbak High Temp. Wear Compound | Loctite® | Epoxy | Nordbak |
| NuSil MED-6385 | NuSil Technology | Silicone | NuSil |
| Aegis® H135ZP | Honeywell | Nylon 6 | Aegis® |
| E-FLEX™ S4060 | Mando Advanced Materials Co., Ltd. | TPE | E-FLEX™ |
| ELASTOSIL® E 60 N grey | Wacker Chemie AG | Silicone | ELASTOSIL® E |