Michimid K4200MN40
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michimid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GmRsAr_Michimid-K4200MN40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michimid K4200MN40 is a Polyamide 66 (Nylon 66) product filled with 40% mineral. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus - Tangent | 6550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 199 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 293 | °C | |
| Middle Temperature | 288 | °C | |
| Front Temperature | 288 | °C | |
| Nozzle Temperature | 282 | °C | |
| Processing (Melt) Temp | 288 | °C | |
| Mold Temperature | 66.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AB1005C | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| SAXALAC™ 340Q | SAX Polymers | ABS | SAXALAC™ |
| CALIBRE™ 5201-8 | Trinseo | PC | CALIBRE™ |
| DIC.PPS Z-200-E5 | DIC Corporation | PPS | DIC.PPS |
| Leona™ 94N05 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |