Durethan® DP 1801/30 H3.0 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Glv9yQ_Durethan-DP-1801-30-H3-0-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.40 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 2.00 mm 1 | 0.70 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.20 | -- | % | |
| Flow : 260°C, 2.00 mm 3 | 0.60 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.20 | -- | % | |
| Water Absorption (Saturation, 23°C) | 5.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 194 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7600 | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress | ||||
| Yield, 23°C | 96.0 | 50.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 93.0 | 47.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ||||
| Yield, 23°C | 2.4 | 9.7 | % | ISO 527-2/50 |
| Break, 23°C | 4.0 | 28 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7300 | 3200 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 170 | 65.0 | MPa | |
| 23°C 6 | 170 | 75.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 6.9 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFHR, 14-080, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | -- | kJ/m² | |
| -30°C | < 10 | -- | kJ/m² | |
| 23°C | < 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 50 | 84 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | < 10 | -- | kJ/m² | |
| -30°C | < 10 | -- | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 35 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 6.1E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 38 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 1 | -- | UL 746 | |
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 725 | -- | °C | |
| Oxygen Index 9 | 30 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| E-FLEX™ I3265 | Mando Advanced Materials Co., Ltd. | EAA | E-FLEX™ |
| Hifax ETA3104HF | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ STAT-KON™ DX10315C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| OmniPro™ CPP TF20 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |
| LNP™ THERMOCOMP™ EC005 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |